Our advantage
1 100% raw material, HIP-Sintered
2 No porosity, no crack
3 Good wear resistance, long working life
4 High bending strength, good impact resistance
5 Finish grinding, concentricity of O.D and I.D
6 Good corrosion resistance
7 Big production capacity, delivery time within 3 ~ 15 days
8 Strong technical support, good after sale service
Grades
Other grades of tungsten carbide forging dies can be offered according to customers' requirement
Production process
Mixture(WC+CO+alcohol)→wet grinding→ drying→grinding again→suppression(Oil press,Automatic hydraulic press)→QC for blank→rubber extrusion→Wc+Co→sintering(HIP )→tungsten carbide blank→Fine grinding→QC→packing.
Welcome for your inquiry!
1 100% raw material, HIP-Sintered
2 No porosity, no crack
3 Good wear resistance, long working life
4 High bending strength, good impact resistance
5 Finish grinding, concentricity of O.D and I.D
6 Good corrosion resistance
7 Big production capacity, delivery time within 3 ~ 15 days
8 Strong technical support, good after sale service
Grades
| GRADE | DENSITY (g/cm3) | TRS (N/mm2) | HARDNESS (HRA) | Application recommended |
| YG11 | 14.4 | 2600 | 88.5 | Forming or stamping dies for metal powders and nonmetal powders. |
| YG15 | 14.0 | 2800 | 87.5 | For fabricating drawing dies of steel tubes and rods under High compressibility ratio; punching,stamping,forging tools under large stress. |
| YG20 | 13.5 | 3200 | 85.5 | For fabricating of stamping dies for watch parts, spring plates of musical instruments, battery jars, small sized steel balls, screws, screw caps. |
| YG16C | 13.9 | 2900 | 85.5 | Impact resistance forging dies. |
| G18C | 13.7 | 3100 | 84.5 | Impact resistance forging dies, hot-press forging dies and rollers. |
| YG20C | 13.5 | 3300 | 83.5 | Dies for wear resistant or impact resistant application. |
| YG22C | 13.3 | 3500 | 83.0 | Nut forming dies and high impact resistance forging dies |
| YG25C | 13.1 | 3600 | 82.5 | Stainless bolt header dies and rollers. |
Production process
Mixture(WC+CO+alcohol)→wet grinding→ drying→grinding again→suppression(Oil press,Automatic hydraulic press)→QC for blank→rubber extrusion→Wc+Co→sintering(HIP )→tungsten carbide blank→Fine grinding→QC→packing.
Welcome for your inquiry!